Customized ITO Conductive Glass Products About Qunguan We can also laser etch ito & fto glass or ITO-PET film. About Qunguan ITO glass The products of the above specifications are all cut by CNC or laser, the size is accurate, and it is suitable for Lab R&D，such as electrochemical polymerization (ECP) You can also provide engineering drawings, we will customize processing for you， laser etching, laser surface notching,laser drilling, ITO has been used to mount cryosections of mouse brain and heart, ITO coverslips can be used to seal digital microfluidic devices, and some other uses that have been reported are: 1. Eumelanin samples prepared on ITO-blocked glass substrates. 2. The interface window of the liquid cell used for beam deflection (OBD) sensing contains a 20nm thick indium tin oxide film. 3. Mesoporous TiO2 film is formed on ITO conductive glass 15mm×20mm×1.1mm 25mm×75mm×0.7mm ito glass etched 50mm×50mm×1.1mm 50mm×50mm×2.2mm 100mm×200mm Add to Cart Add to Cart Add to Cart Add to Cart Buying Options Add to Cart Customer Reviews 5.0 out of 5 stars 1 4.4 out of 5 stars 2 — 4.6 out of 5 stars 2 4.0 out of 5 stars 3 5.0 out of 5 stars 3 Price $92.00$92.00 $98.00$98.00 $143.65$143.65 $35.91$35.91 — no data $22.90$22.90 Resistivity ＜15 ohm/sq ＜10 ohm/sq ＜15 ohm/sq ＜10 ohm/sq ＜10 ohm/sq ＜5 ohm/sq Coating Thickness 135nm 185nm 135nm 185nm 500nm 1200nm Product name ITO glass ITO glass ITO glass ITO glass FTO glass ITO - PET film What method can be used to etch Product , Indium tin oxide coated glass slide? An aqueous solution of 20% hydrochloric acid, 5% nitric acid and a few drops of liquid detergent to promote wetting of the ITO surface will remove ITO. If this solution is heated to 55°C, it will typically etch 100 ohm ITO coating in 30-60 seconds, or if the etching is carried out at room temperature, it will take six to ten minutes. Differences in the morphology of the coating, the thickness of the coating (more conductive coatings will be thicker), and changes in the purity or concentration of the acid solution will effect the time required to remove the ITO. Please be advised that ITO coatings can be lost if they come into direct contact with mineral acids and strong organic acids. Therefore, direct contact with these agents should be avoided. After the etching process is complete, the slides should be immediately rinsed in a 10% aqueous solution of sodium carbonate to neutralize any residual acid. To avoid water spotting, blow dry the slides with pure nitrogen gas. Regarding the application of indium tin oxide (ITO), The F-22 canopy is tinted yellow is because it has a special coating that reduces its radar visibility and protects the pilot from harmful electromagnetic waves. The coating is made of a material just is indium tin oxide (ITO), which has both transparent and conductive properties, Interested friends can do similar research. More about Qunguan ITO glass The ito glass slide is made with soda lime float glass. Molten glass is floated on a pool of liquid tin under a nitrogen/hydrogen atmosphere. This high volume process results in glass which does not require grinding or polishing to achieve a high-quality finish. Float glass will typically have a strain point of 523°C, a CTE of 77-85 x 107 / °C, and a refractive index of 1.517. Typical composition of float glass is 72.6% SiO2, 0.8% B2O3, 1.7% Al2O3, 4.6% CaO, 3.6% MgO, and 15.2% Na2O. For Product , Indium tin oxide coated glass slide, what is the passivation layer, and what is it's purpose? ITO coated float glass is only offered with a SiO2 passivation layer applied directly on the glass prior to ITO coating. The passivation layer is intended to minimize the leaching of alkali oxides into liquid crystals, which can have a detrimental effect on the volume resistivity of the liquid crystal. 1. Cleaning of conductive glass During the production, packaging and transportation of conductive glass, the surface of the glass may be contaminated by impurities such as dust and grease. Ultrasonic cleaning is generally carried out in the order of: toluene → two ethanol → deionized water The oil on the surface of the glass is insoluble in water, but it is soluble in organic solvents such as toluene, acetone, and ethanol. Among them, toluene has the strongest degreasing ability, so it is first washed with toluene, but toluene cannot remain on the glass surface. Since toluene is soluble in acetone, it can be washed with acetone. Not only can the residual grease be washed away, but toluene is also dissolved. Similarly, acetone does not remain on the surface of the glass. Since acetone is easily soluble in ethanol, it can be washed with ethanol. Ethanol and water are mutually soluble in any ratio, and finally ethanol is dissolved in a large amount of decompressed water. 2. Storage of Conductive Glass ITO/FTO conductive glass should be stored at room temperature, humidity below 65%, and stored dry; the glass should be placed vertically when stored. And conductive glass sheets should be separated by a sheet of paper to prevent sodium ions from penetrating into the IT0 conductive layer of the next sheet (see glass structure) ,while preventing the glass sheets from sticking to each other. Important notes when cleaning Professional anti-acid and alkali appliances must be used, such as Teflon materials. Relationship between square resistance and resistivity and conductivity